Wang, and 10 co-authors, reported in 2020 that a systematic study of the surface chemical properties of uranium minerals was necessary to improve the uranium ore extracting process. The presented work aims to posit that geochemistry and acid hydrometallurgy accessibility of uraninite from the Mianhuakeng (MHK) granite-hosted uranium deposit, South China provides insight on this ore extracting domain.
Mineralogy, geochemical composition, U–Th–Pb chemical age, and uranium deportment of the uraninite were systematically analyzed by using scanning electron microscope with energy dispersion spectrum (SEM-EDS), an electron probe microanalyzer (EPMA), and x-ray photoelectron spectroscopy (XPS).
The results showed that uraninite was intergrowth with coffinite, probably due to uraninite being partly metasomatized into coffinite along the fissures. The major element content of uraninite such as for UO2, SiO2, and CaO were 79.46 ± 2.03 wt%, 6.19 ± 1.36 wt%, and 5.09 ± 0.80 wt%, respectively.
Single-point U–Th–Pb chemical ages for uraninite grains were calculated with the EPMA data, and the results showed ages ranging from a few million to dozens of million years, indicating Pb loss after uraninite formed. Uranium deportment in uraninite generally existed in the forms of UO2, U3O8, and UO3, and mostly showed high valence states suggested by XPS.
Uranium on the surface of the uraninite grain was partially oxidized by sulfuric acid leaching, which led to tetravalent uranium converting to hexavalent uranium, suggesting uraninite in the MHK uranium deposit is accessible to be leached by sulfuric acid.